Ultrasonic micro-arc oxidation enhances Ti-Cu alloy antibacterial and biocompatible properties

Abstract

In order to improve antibacterial properties and cell biocompatibility of Ti-Cu alloy, an ultrasonic micro-arc oxidation (UMAO) has been applied to Ti-Cu alloy. The corrosion resistance, antibacterial activity and cell compatibility of Ti-Cu alloy before and after UMAO were studied in detail by means of electrochemical test, plate count method and CCK-8 test scanning electron microscopy (SEM) technology to evaluate the application possibilities of UMAO as a surface bio-modification method for Ti-Cu alloy. The surface microstructure characterisation showed that a typical porous coating with a pore diameter of 3–8 μm and a thickness of 5–15 μm was formed on the surface of the Ti-Cu alloy, which significantly improved the surface roughness and hydrophilicity. The plate count method demonstrated that UMAO coatings on Ti-Cu alloy showed strong antibacterial activity (≥99%) against Staphylococcus aureus ( S. aureus ) even after being immersed in a physiological saline for up to 20 days, indicating that UMAO-treated Ti-Cu alloy had very strong long-term antibacterial properties. It is believed that the strong long-term antimicrobial properties of Ti-Cu-UMAO samples were mainly due to the formation of Cu 2 O and CuO in UMAO coatings. The results of cell compatibility evaluation showed that UMAO treatment did not bring about cytotoxicity but improved the early adhesion of MC3T3 cell.