Abstract

Silk fibroin (SF)-based electroactive biomaterials with favorable electroconductive property and transparency have great potential applications for cell culture and tissue engineering. Poly(3,4-ethylenedioxythiophene)-poly(styrenesulfonate) (PEDOT:PSS) is an excellent candidate as a conductive component, which has been widely used in the field of bioelectronics; however, it is hard to be directly coated onto the surface of regenerated SF (RSF) materials with good stability under a cell culture environment. In this study, a one-step facile PEDOT:PSS modification approach for RSF films based on a suitable post-treatment process of RSF was developed. PEDOT:PSS was successfully embedded and fixed into the shallow surface of an RSF film, forming a tightly conjunct conductive layer on the film surface based on the conformation transition of RSF during the post-treatment process. The conductive layer demonstrated a PSS-rich surface and a PEDOT-rich bulk structure and showed excellent stability under a cell culture environment. More specifically, the robust RSF/PEDOT:PSS film achieved in the post-treatment formula with 70% ethanol proportion possessed best comprehensive properties such as a sheet resistance of 3.833 × 103 Ω/square, a conductivity of 1.003 S/cm, and transmittance over 80% at maximum in the visible range. This kind of electroactive biomaterial also showed good electrochemical stability and degradable properties. Moreover, pheochromocytoma-derived cell line (PC12) cells were cultured on the RSF/PEDOT:PSS film, and an effective electrical stimulation cell response was demonstrated. The facile preparation strategy and the good electroconductive property and transparency make this RSF/PEDOT:PSS film an ideal candidate for neuronal tissue engineering and further for biomedical applications.